Additive manufacture of lightly crosslinked semicrystalline thiol-enes for enhanced mechanical performance.

Photopolymerizable semicrystalline thermoplastics resulting from thiol-ene polymerizations were formed via fast polymerizations and achieved excellent mechanical properties. These materials have been shown to produce materials desirable for additive manufacturing (3D printing), especially for recyclable printing and investment casting. However, while well-resolved prints were previously achieved with the thiol-ene thermoplastics, the remarkable elongation at break (ϵmax) and toughness (T) attained in bulk were not realized for 3D printed components (ϵmax,bulk ~ 790%, Tbulk ~ 102 MJ m-3 vs. ϵmax,print < 5%, Tprint < 0.5 MJ m-3). In this work, small concentrations (5-10 mol%) of a crosslinker were added to the original thiol-ene resin composition without sacrificing crystallization potential to achieve semicrystalline, covalently crosslinked networks with enhanced mechanical properties. Improvements in ductility and overall toughness were observed for printed crosslinked structures, and substantial mechanical augmentation was further demonstrated with post-manufacture thermal conditioning of printed materials above the melting temperature (Tm). In some instances, this thermal conditioning to reset the crystalline component of the crosslinked prints yielded mechanical properties that were comparable or superior to its bulk counterpart (ϵmax ~ 790%, T ~ 95 MJ m-3). These unique photopolymerizations and their corresponding monomer compositions exhibited concurrent polymerization and crystallization along with mechanical properties that were tunable by changes to the monomer composition, photopolymerization conditions, and post-polymerization conditioning. This is the first example of a 3D printed semicrystalline, crosslinked material with thermally tunable mechanical properties that are superior to many commercially-available resins.

Rational Design of Efficient Amine Reductant Initiators for Amine-Peroxide Redox Polymerization.

Amine-peroxide redox polymerization (APRP) has been highly prevalent in industrial and medical applications since the 1950s, yet the initiation mechanism of this radical polymerization process is poorly understood so that innovations in the field are largely empirically driven and incremental. Through a combination of computational prediction and experimental analysis, we elucidate the mechanism of this important redox reaction between amines and benzoyl peroxide for the ambient production of initiating radicals. Our calculations show that APRP proceeds through SN2 attack by the amine on the peroxide but that homolysis of the resulting intermediate is the rate-determining step. We demonstrate a correlation between the computationally predicted initiating rate and the experimentally measured polymerization rate with an R2 = 0.80. The new mechanistic understanding was then applied to computationally predict amine reductant initiators with faster initiating kinetics. This led to our discovery of N-(4-methoxyphenyl)pyrrolidine (MPP) as amine reductant, which we confirmed significantly outperforms current state-of-the-art tertiary aromatic amines by ∼20-fold, making it the most efficient amine-peroxide redox initiator to date. The application of amines with superior kinetics such as MPP in APRP could greatly accelerate existing industrial processes, facilitate new industrial manufacturing methods, and improve biocompatibility in biomedical applications conducted with reduced initiator concentrations yet higher overall efficiency.

A readily programmable, fully reversible shape-switching material.

Liquid crystalline (LC) elastomers (LCEs) enable large-scale reversible shape changes in polymeric materials; however, they require intensive, irreversible programming approaches in order to facilitate controllable actuation. We have implemented photoinduced dynamic covalent chemistry (DCC) that chemically anneals the LCE toward an applied equilibrium only when and where the light-activated DCC is on. By using light as the stimulus that enables programming, the dynamic bond exchange is orthogonal to LC phase behavior, enabling the LCE to be annealed in any LC phase or in the isotropic phase with various manifestations of this capability explored here. In a photopolymerizable LCE network, we report the synthesis, characterization, and exploitation of readily shape-programmable DCC-functional LCEs to create predictable, complex, and fully reversible shape changes, thus enabling the literal square peg to fit into a round hole.

Multiple patterning of holographic photopolymers for increased refractive index contrast.

We demonstrate that multiple exposures of a two-component holographic photopolymer can quadruple the refractive index contrast of the material beyond the single-exposure saturation limit. Quantitative phase microscopy of isolated structures written by laser direct-write lithography is used to characterize the process. This technique reveals that multiple exposures are made possible by diffusion of the chemical components consumed during writing into the previously exposed regions. The ultimate index contrast is shown to be limited by the solubility of fresh components into the multiply exposed region.